REAFREE. Saturated Carboxylated Polyesters for Hybrid Systems. RATIO 60/40 (July, 2003)
| REAFREE |
Curing
t (min.)/
T (oC) oven |
Gardner
color
ASTM
D-1544 |
Glass transition
temp
(DSC) (oC) |
Melt viscosity
165oC ICI
Cone-plate (Pa.s) |
Acid value
ASTM
D-1639
(mgKOH/g) |
Characteristics |
| 6600* |
10/200 |
max. 2 |
approx. 51 |
7.5 - 20 |
50 - 55 |
Excellent flow, slow cure rate. General purpose resin without TMA. |
| 6604 |
10/200 |
max. 3 |
approx. 52 |
14 - 20 |
51 - 56 |
Good flow, moderate cure rate. Good chemical resistance. |
| 6605 |
12/200 |
max. 3 |
approx. 51 |
9 - 12 |
61 - 65 |
Excellent flow, slow cure rate. Good chemical resistance. Semi-gloss finishes with matting agent DT-125 (VANTICO). |
| 6615 |
12/210 |
max. 3 |
approx. 51 |
9 - 12 |
61 - 65 |
Slow curing type of 6605. |
| 6660* |
10/160 |
max. 2 |
approx. 49 |
7.5 - 20 |
50 - 55 |
High reactivity, without TMA. |
| 6680* |
10/180 |
max. 2 |
approx. 49 |
7.5 - 20 |
50 - 55 |
Good balance between cure and flow, without TMA. |
| 6682 |
10/180 |
max. 4 |
approx. 65 |
13 - 30 |
50 - 55 |
Good combination of cure and flow. |
| 6684 |
10/180 |
max. 3 |
approx. 52 |
12 - 20 |
50 - 56 |
Higher reactivity than 6604. |
| 6685 |
12/180 |
max. 3 |
approx. 51 |
9 - 12 |
61 - 65 |
Higher reactivity than 6605. |
| 6687 |
10/180 |
max. 3 |
approx. 46 |
9 - 14 |
48 - 53 |
High flexibility, 0T. For PCM interior use. |
ALL POLYESTER RESINS CAN BE SUPPLIED FOR TRIBOCHARGING GUNS (-T version), GAS-OVEN STABILIZED (-S version) or BOTH (-TS version).
*TMA free.
|